Method for forming semiconductor structure

ABSTRACT

A method for forming a semiconductor structure is provided. The method includes following operations. A layer stack is formed over the substrate. The formation of the layer stack includes the following sub-operations: a blocking layer is formed over the substrate, a lower conductive layer is formed over the blocking layer, a first seed layer is formed over the lower conductive layer, a ferroelectric layer is formed over the first seed layer, and an upper conductive layer is formed over the ferroelectric layer. The layer stack is patterned to form a gate stack over the substrate. A spacer layer is formed over sidewalls of the gate stack. A pattered interlayer dielectric layer is formed over the substrate and the gate stack. A source region and a drain region are formed in the substrate through the patterned interlayer dielectric layer.

PRIORITY CLAIM AND CROSS-REFERENCE

This application is a divisional application of U.S. patent application Ser. No. 17/238,925 filed on Apr. 23, 2021. entitled of “SEMICONDUCTOR STRUCTURE AND METHOD FOR FORMING THE SAME”; this application is incorporated herein by reference in their entireties.

BACKGROUND

With advantages of non-volatility, low power consumption, short programming time, and high readiwrite endurance, ferroelectric random-access memory (FeRAM) has drawn increasing attention.

FeRAM can be categorized into two types. One type is made of transistors connected with capacitors, such as 1T1C or chain FeRAM structures. The other type is a field-effect transistor (FET), and is referred to as a ferroelectric memory field-effect transistor (FeMFET). The structure of the FeMFET is similar to that of the metal-oxide-semiconductor field-effect transistor (MOSFET), but the FeMFET uses a ferroelectric material as a part of its gate dielectric.

One type of a FeMFET has an MFS-FET structure in which the gate dielectric is formed using a ferroelectric layer rather than oxide. However, it is found that MFS structures suffer from interface reactions between ferroelectric materials and semiconductor substrates, high leakage current, retention, and fatigue. Another type of FeMFET has a metal-ferroelectric-insulator-silicon-FET (MFIS-FET) structure with an insulating layer separating the ferroelectric layer from the semiconductor substrate. A third type of FeMFET is a metal-ferroelectric-metal-insulator-semiconductor-FET (MFMIS FET) structure.

BRIEF DESCRIPTION OF THE DRAWINGS

Aspects of the present disclosure are best understood from the following detailed description when read with the accompanying figures. It is noted that, in accordance with the standard practice in the industry, various features are not drawn to scale. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.

FIG. 1 illustrates a schematic cross-sectional view of a semiconductor structure in accordance with some embodiments of the present disclosure.

FIG. 2 illustrates a schematic cross-sectional view of a semiconductor structure in accordance with some embodiments of the present disclosure.

FIG. 3 illustrates a schematic cross-sectional view of a semiconductor structure in accordance with some embodiments of the present disclosure.

FIG. 4 illustrates a schematic cross-sectional view of a semiconductor structure in accordance with some embodiments of the present disclosure.

FIG. 5 illustrates a flowchart of a method for forming a semiconductor structure in accordance with some embodiments of the present disclosure.

FIGS. 6A to 6M illustrate schematic cross-sectional views of a semiconductor structure at various stages of fabrication in accordance with some embodiments of the present disclosure.

FIGS. 7A to 7M illustrate schematic cross-sectional views of a semiconductor structure at various stages of fabrication in accordance with some embodiments of the present disclosure.

FIG. 8 illustrates a schematic cross-sectional view of a semiconductor structure as shown in FIG. 6L integrated with an FET device in accordance with some embodiments of the present disclosure.

DETAILED DESCRIPTION

The following disclosure provides many different embodiments, or examples, for implementing different features of the provided subject matter. Specific examples of elements and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.

Further, spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper,” “on” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. The spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. The apparatus may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein may likewise be interpreted accordingly.

As used herein, although the terms such as “first,” “second” and “third” describe various elements, components, regions, layers and/or sections, these elements, components, regions, layers and/or sections should not be limited by these terms. These terms may be only used to distinguish one element, component, region, layer or section from another. The terms such as “first,” “second” and “third” when used herein do not imply a sequence or order unless clearly indicated by the context.

Notwithstanding that the numerical ranges and parameters setting forth the broad scope of the disclosure are approximations, the numerical values set forth in the specific examples are reported as precisely as possible. Any numerical value, however, inherently contains certain errors necessarily resulting from the standard deviation found in the respective testing measurements. Also, as used herein, the terms “substantially,” “approximately” or “about” generally mean within a value or range that can be contemplated by people having ordinary skill in the art. Alternatively, the terms “substantially,” “approximately” or “about” mean within an acceptable standard error of the mean when considered by one of ordinary skill in the art. People having ordinary skill in the art can understand that the acceptable standard error may vary according to different technologies. Other than in the operating/working examples, or unless otherwise expressly specified, all of the numerical ranges, amounts, values and percentages such as those for quantities of materials, durations of times, temperatures, operating conditions, ratios of amounts, and the likes thereof disclosed herein should be understood as modified in all instances by the terms “substantially,” “approximately” or “about.” Accordingly, unless indicated to the contrary, the numerical parameters set forth in the present disclosure and attached claims are approximations that can vary as desired. At the very least, each numerical parameter should be construed in light of the number of reported significant digits and by applying ordinary rounding techniques. Ranges can be expressed herein as from one endpoint to another endpoint or between two endpoints. All ranges disclosed herein are inclusive of the endpoints, unless specified otherwise.

An MFMIS FET structure may serve as a portion of a transistor with a metal-ferroelectric-metal (MFM) stack serving as a gate structure over an insulator on a semiconductor channel. In some comparative embodiments, the MFMIS FET structure may use single-crystal lead zirconate titanate (PZT) or barium strontium titanate (SBT). The thickness of the PZT or SBT influences performance of the MFMIS FET structure. For example, a thicker ferroelectric layer may result in a greater resistance value and a lower capacitance value. The thickness of the ferroelectric layer also affects multi-domain characteristics of the MFM stack. Therefore, an MFMIS FET structure with a thinner ferroelectric layer is desired. It is desired that the remnant polarization of the ferroelectric layer is promoted and the electron or hole injection from channel to the gate is reduced. It is also desired that the crystallinity of the ferroelectric layer is stabilized.

The present disclosure therefore provides a semiconductor structure and a method for forming the same. In some embodiments, the semiconductor structure may be an MFMIS memory structure. In some embodiments, the semiconductor structure includes a top-gate structure. In some embodiments, the MFMIS memory structure includes a hafnium zirconium oxide (HfZrO)-based ferroelectric layer that may be formed by atomic layer deposition (ALD). Accordingly, a thinner ferroelectric layer is obtained by ALD. Thus, the feasibility of the MFMIS memory structure is further improved.

Refer to FIG. 1. FIG. 1 illustrates a schematic cross-sectional view of a semiconductor structure 100. The semiconductor structure 100 includes a substrate 102, a gate stack 106 over the substrate 102 and a blocking layer 104 between the substrate 102 and the gate stack 106 in accordance with some embodiments of the present disclosure. In some embodiments, the gate stack 106 may include an upper electrode 1069, a lower electrode 1061, a ferroelectric layer 1065, and a first seed layer 1063. In some embodiments, the ferroelectric layer 1065 may be disposed between the upper electrode 1069 and the lower electrode 1061. In some embodiments, the first seed layer 1063 may be disposed between the ferroelectric layer 1065 and the lower electrode 1061.

In some embodiments, the substrate 102 may include a semiconductor material. In some embodiments, the semiconductor material may include silicon. Alternatively, the substrate 102 may include other elementary semiconductor such as germanium (Ge) in accordance with some embodiments of the present disclosure. In some embodiments, the substrate 102 may additionally or alternatively include a compound semiconductor such as silicon carbide (SiC), silicon oxide, gallium arsenide (GaAs), indium arsenide (InAs), indium phosphide (InP), or a combination thereof. In some embodiments, the substrate 102 may include an alloy semiconductor such as silicon germaniwn (SiGe), silicon germanium carbide (SiGeC), gallium arsenic phosphide (GaAsP), and gallium indium phosphide (GaInP).

In some embodiments, the substrate 102 may be a silicon-on-insulator (SOI) substrate. Generally, an SOI substrate includes a layer of a semiconductor material (e.g., silicon, germanium and/or the like) formed on an insulator layer. In some embodiments, the insulator layer may be, for example, a buried oxide (BOX) layer or a silicon oxide layer. In some embodiments, other substrates that may be used include multi-layered substrates, gradient substrates, hybrid orientation substrates, any combinations thereof and/or the like.

In some embodiments, the blocking layer 104 may be disposed between the gate stack 106 and the substrate 102. In some embodiments, the blocking layer 104 may include doped hafnium oxide. In some embodiments, the blocking layer 104 including doped hafnium oxide may reduce electron or hole injection from a channel region 116 to the gate stack 106. In some embodiments, the doped hafnium oxide may include Si, Mg, AL, Y₂O₃, La, Sr, Gd, N, Sc, Ca or a combination thereof. In some embodiments, the doped hafnium oxide may include Si. In some embodiments, the doped hafnium oxide may include Si in a proportion of from approximately 1% to approximately 90%. In some embodiments, the doped hafnium oxide may include Si in a proportion of from approximately 20% to approximately 60%. In some embodiments, the blocking layer 104 has a thickness of from approximately 0.1 nanometers to approximately 10 nanometers.

In some embodiments, the upper electrode 1069 and/or the lower electrode 1061 may be formed with tensile stress. In some embodiments, the upper electrode 1069 and/or the lower electrode 1061 with tensile stress may stabilize the ferroelectric layer 1065. In some embodiments, the upper electrode 1069 and/or the lower electrode 1061 with tensile stress may stabilize the o-phase of the ferroelectric layer 1065. In some embodiments, the upper electrode 1069 and the lower electrode 1061 may include a conductive material. In some embodiments, the conductive material may have a coefficient of thermal expansion (CTE) smaller than that of the ferroelectric layer 1065. For example, the upper electrode 1069 and the lower electrode 1061 may include a conductive material having a coefficient thermal expansion (CTE) less than that of o-phase ferroelectric layer 1065. In some embodiments, the upper electrode 1069 and/or the lower electrode 1061 may include a metal, a metal nitride, a metal alloy or a combination thereof. In some embodiments, the upper electrode 1069 and/or the lower electrode 1061 may include platinum (Pt), titanium (Ti), titanium nitride (TiN), tantalum (Ta), tantalum nitride (TaN), tungsten (W), iron (Fe), nickel (Ni), beryllium (Be), chromium (Cr), cobalt (Co), antimony (Sb), iridium (Ir), molybdenum (Mo), osmium (Os), thorium (Th), vanadium (V), an alloy thereof, or a combination thereof. In some embodiments, the upper electrode 1069 and/or the lower electrode 1061 may have a thickness of from approximately 15 nanometers to approximately 500 nanometers. In some embodiments, the lower electrode 1061 and/or the upper electrode 1069 may be annealed by a post metal anneal (PMA) in an ambient air of nitrogen, argon, oxygen or a combination thereof. In some embodiments, the upper electrode 1069 and the lower electrode 1061 may include the same conductive material. In some alternative embodiments, the upper electrode 1069 and the lower electrode 1061 may include different conductive materials.

In some embodiments, the first seed layer 1063 may be formed in a single-layer form or a multi-layered form. In some embodiments, the first seed layer 1063 may include a metal oxide. In some embodiments, the first seed layer 1063 may include zirconium oxide of cubic-phase (c-phase), tetragonal phase (t-phase) or orthorhombic phase (o-phase), zirconium yttrium oxide of c-phase, t-phase or o-phase, hafnium oxide of c-phase, t-phase or o-phase, aluminum oxide of c-phase, t-phase or o-phase, and hafnium zirconium oxide of c-phase, t-phase or o-phase. For example, the first seed layer 1063 may include c-phase, t-phase or o-phase zirconium dioxide (ZrO₂), c-phase, t-phase or o-phase zirconium dioxide and diyttuim trioxide (ZrO₂—Y₂O₃), c-phase, t-phase or o-phase hafnium dioxide (HfO₂), c-phase, t-phase or o-phase dialuminum trioxide (Al₂O₃), c-phase, t-phase or o-phase hafnium zirconium oxide (Hf_(x)Zr_(1-x)O₂), or a combination thereof, wherein x of Hf_(x)Zr_(1-x)O₂ can be varied from 0 to 1. In some embodiments, the first seed layer 1063 may have a thickness of from approximately 0.1 nanometer to approximately 5 nanometers. in the case where the first seed layer 1063 has a thickness less than 0.1 nanometer, the first seed layer 1063 may not be crystallized. However, if the first seed layer 1063 has a thickness more than 0.5 nanometers, the first seed layer 1063 may have a monoclinic phase, which is undesired. In some embodiments, the first seed layer 1063 may promote the remnant polarization (2 Pr, wherein 2 Pr=Pr⁺−Pr⁻) of the ferroelectric layer 1065. In some embodiments, the first seed layer 1063 may be annealed. In some embodiments, the first seed layer 1063 may be annealed by an in-situ annealing process. In some embodiments, after the annealing process, the first seed layer 1063 may have increased crystallinity.

In some embodiments, the ferroelectric layer 1065 has a thickness of from approximately 0.1 nanometer to approximately 100 nanometers. In some embodiments, the ferroelectric layer 1065 includes hafnium zirconium oxide Hf_(x)Zr_(1-x)O₂, where x may be any value between 0 and 1. In some embodiments, the ferroelectric layer 1065 may include one or more oxygen vacancies. In some embodiments, the ferroelectric layer 1065 may include Hf_(x)Zr_(1-x)O₂ of cubic-phase (c-phase), tetragonal phase (t-phase), orthorhombic phase (o-phase), monoclinic phase (m-phase), or a combination thereof. In some embodiments, the ferroelectric layer 1065 may include aluminum nitride (AlN) doped with Sc or other ferroelectricity elements. In some embodiments, the ferroelectric layer 1065 may include Hf_(x)Zr_(1-x)O₂ being doped with silicon (Si), Al, or ions of larger radius, such as lanthanum (La), scandium (Sc), calcium (Ca), barium (Ba), gadolinium (Gd), strontium (Sr), or yttrium to increase remnant polarization (2 Pr, wherein 2Pr=Pr⁺−Pr⁻). In some embodiments, the ferroelectric layer 1065 may include may include c-phase, t-phase, o-phase, and m-phase Hf_(0.5)Zr_(0.5)O₂, with the c-, t-, o-phase Hf_(0.5)Zr_(0.5)O₂ being greater than 50% compared to m-phase Hf_(0.5)Zr_(0.5)O₂, but the disclosure is not limited thereto.

In some embodiments, the semiconductor structure 100 may further include a spacer layer 108. In some embodiments, the spacer layer 108 may be disposed on side walls of the gate stack 106 and the blocking layer 104. In some embodiments, the spacer layer 108 may include a silicon-containing material, such as silicon oxide, silicon nitride or a combination thereof. In some embodiments, the spacer layer 108 may include Si₃N₄, SiO₂, or a combination thereof.

In some embodiments, the semiconductor structure 100 may further include an interlayer dielectric (ILD) layer 114. In some embodiments, the interlayer dielectric layer 114 may be disposed over the substrate 102 and the gate stack 106. In some embodiments, the interlayer dielectric layer 114 may be patterned to define dimensions and locations for a source region contact 120 which may be in contact with a source region 110, a drain region contact 122 which may be in contact with a drain region 112, and a gate region contact 124 which may be in contact with a top surface of the gate stack 106. In some embodiments, the source region contact 120, drain region contact 122 and gate region contact 124 may include a conductive material. In some embodiments, the conductive material may include a metal, a metal nitride, a metal alloy or a combination thereof.

In some embodiments, the gate stack 106 of the semiconductor structure 100 may further include a second blocking layer (not shown). In some embodiments, the second blocking layer may be disposed between the first seed layer 1063 and the upper electrode 1069. In some embodiments, the second blocking layer may be disposed between the first seed layer 1063 and the ferroelectric layer 1065. In some embodiments, the second blocking layer may be disposed between the ferroelectric layer 1065 and the upper electrode 1069. In some embodiments, the second blocking layer may include a doped metal oxide, such as doped Ta₂O₅ or doped. HfO₂. In some embodiments, the doped Ta₂O₅ or doped HfO₂ may include Si, Mg, Al Y₂O₃, La, Sr, Gd, N, Sc, Ca or a combination thereof. In some embodiments, the second blocking layer may have a thickness of from 0.1 nanometer to 1 nanometer.

In some embodiments, the semiconductor structure 100 may be electrically separated from other semiconductor structures by an isolation structure 118. The isolation structure may include a shallow trench isolation (STI), but the disclosure is not limited thereto.

Refer to FIG. 2. FIG. 2 illustrates a schematic cross-sectional view of a semiconductor structure 200 including a gate stack 106 over a substrate 302 and a blocking layer 104 in accordance with some embodiments of the present disclosure. In some embodiments, compared to the semiconductor structure 100 as shown in FIG. 1, the gate stack 106 of the semiconductor structure 200 may further include a second seed layer 1067. In some embodiments, the second seed layer 1067 may be disposed between the ferroelectric layer 1065 and the upper electrode 1069. In some embodiments, the second seed layer 1067 may include a metal oxide. In some embodiments, the second seed layer 1067 may include zirconium oxide of cubic-phase (c-phase), tetragonal phase (t-phase) or orthorhombic phase (o-phase), zirconium yttrium oxide of c-phase, t-phase or o-phase, hafnium oxide of c-phase, t-phase or o-phase, aluminum oxide of c-phase, t-phase or o-phase, and hafnium zirconium oxide of c-phase, t-phase or o-phase. For example, the second seed layer 1067 may include c-phase, t-phase or o-phase zirconium dioxide (ZrO₂), c-phase, t-phase or o-phase zirconium dioxide and diyttuim trioxide (ZrO₂—Y₂O₃), c-phase, t-phase or o-phase hafnium dioxide (HfO₂), c-phase, t-phase or o-phase diatuminum trioxide (Al₂O₃), c-phase, t-phase or o-phase hafnium zirconium oxide (Hf_(x)Zr_(1-x)O_(y)), or a combination thereof, wherein x of Hf_(x)Zr_(1-x)O_(y) can be varied from 0 to 1. In some embodiments, the second seed layer 1067 may have a thickness of from approximately 0.1 nanometer to approximately 5 nanometers. In the case where the second seed layer 1067 has a thickness less than 0.1 nanometer, the second seed layer 1067 may not be crystallized. However, if the second seed layer 1067 has a thickness more than 0.5 nanometers, the second seed layer 1067 may have a monoclinic phase, which is undesired.

In some embodiments, the gate stack 106 of the semiconductor structure 200 may further include a second blocking layer (not shown). In some embodiments, the second blocking layer may be disposed between the first seed layer 1063 and the second seed layer 1067. In some embodiments, the second blocking layer may be disposed between the first seed layer 1063 and the ferroelectric layer 1065. In some embodiments, the second blocking layer may be disposed between the ferroelectric layer 1065 and the second seed layer 1067. In some embodiments, the second blocking layer may include a doped metal oxide, such as doped tantalum oxide (Ta₂O₅), a doped hafnium oxide (HfO₂), or a combination thereof. In some embodiments, the doped Ta₂O₅ or doped HfO₂ may include Si, Mg, Al Y₂O₃, La, Sr, Gd, N, Sc, Ca or a combination thereof. In some embodiments, the second blocking layer may have a thickness of from approximately 0.1 nanometer to approximately 1 nanometer.

Refer to FIG. 3. FIG. 3 illustrates a schematic cross-sectional view of a semiconductor structure 300. In some embodiments, the semiconductor structure 300 may include a substrate 302, a buffer layer 304 over the substrate 302, a channel layer 306 over the buffer layer 304, a gate stack 106 over channel layer 306, and a blocking layer 104 between the gate stack 106 and the channel layer 306 in accordance with some embodiments of the present disclosure. In some embodiments, the gate stack 106 and the blocking layer 104 of the semiconductor structure 300 may be defined in accordance with those described above for the semiconductor structure 100. In some embodiments, the substrate 302 may include a metal oxide semiconductor, such as indium gallium zinc oxide (IGZO). In some embodiments, the IGZO may be amorphous IGZO (α-IGZO).

In some embodiments, the buffer layer 304 may be disposed between the substrate 302 and the channel layer 306. In some embodiments, the buffer layer 304 may include a metal oxide, such as HfO_(x), ZrO_(x), SiO_(x), AlO_(x), MgO or combinations thereof. A thickness of the buffer layer 304 may be between approximately 0.1 nanometers and approximately 1 nanometer, hut the disclosure is not limited thereto. In some embodiments, the buffer layer 304 may provide a better adhesion for the channel layer 306 and the substrate 302. In some embodiments, the buffer layer may reduce the electron or hole injection from the channel layer 306 to the substrate 302.

In some embodiments, the channel layer 306 may include Si, Ge, SiGe, a-IGZO, IZO, SnIGZO, GaN, AlInAs, GaAs or combinations thereof. A thickness of the channel layer 306 may be between approximately 1 nanometer and approximately 150 nanometers, but the disclosure is not limited thereto. The channel layer 306 is of the function of current generation. In some embodiments, the semiconductor structure may further include a source region 305 and a drain region 310. In some embodiments, the source region 305 and the drain region 310 may be disposed over the substrate 302. In some embodiments, the source region 305 and the drain region 310 may be disposed within the channel layer 306.

In some embodiments, the gate stack 106 of the semiconductor structure 300 may further include a second blocking layer (not shown) as defined above with respect to FIG. 1.

Refer to FIG. 4. FIG. 4 illustrates a schematic cross-sectional view of a semiconductor structure 400 including a gate stack 106 over a substrate 302 and a blocking layer 104 in accordance with some embodiments of the present disclosure. In some embodiments, compared to the semiconductor structure 300 as shown in FIG. 3, the gate stack 106 of the semiconductor structure 400 may further include a second seed layer 1067. In some embodiments, the second seed layer 1067 may be defined as described above with respect to the semiconductor structure 200 shown in FIG. 2.

In some embodiments, the semiconductor structure 400 may further include a second blocking layer (not shown) as defined above with respect to FIG. 2.

Refer to FIG. 5. FIG. 5 illustrates a flowchart of a method for forming a semiconductor structure 500 according to aspects of the present disclosure. The method 500 includes a number of operations and will be further described according to one or more embodiments. It should be noted that the operations of the method 500 may be rearranged or otherwise modified within the scope of the various aspects. It should be further noted that additional processes may be provided before, during, and after the method 500, and that some other processes may just be briefly described herein. Thus, other implementations are possible within the scope of the various aspects described herein.

The method 500 begins with operation 502 in which a layer stack in formed over a substrate 102. In some embodiments, at least an isolation structure 118 may be formed in the substrate 102. The isolation structure 118 is formed in the substrate 102 for defining a dimension and a location of a MFMIS structure. Referring to FIG. 6A, in some embodiments, the operation 502 of the method 500 may begin with operation 5021 in which a blocking layer 104 is formed over the substrate 102. In some embodiments, the blocking layer 104 may be formed using chemical vapor deposition (CVD), physical vapor deposition (PVD) or atomic layer deposition (ALD). In some embodiments, the blocking layer 104 may be formed by ALD.

Referring to FIG. 6B, in some embodiments, the operation 502 of the method 500 proceeds with operation 5023, in which a lower conductive layer 1061 is formed over the blocking layer 104. In some embodiments, the lower conductive layer 1061 may be formed using CVD, PVD or ALD, but the disclosure is not limited thereto. In some embodiments, the lower conductive layer 1061 may be annealed. In some embodiments, the lower conductive layer 1061 is annealed by post metal annealing (PMA). In some embodiments, the lower conductive layer 1061 is annealed by PMA at a temperature of from 400° C. to 900° C. In some embodiments, the lower conductive layer 1061 may be annealed by PMA in an ambient air of nitrogen, argon, oxygen or a combination thereof.

Referring to FIG. 6C, in some embodiments, the operation 502 of the method 500 proceeds with operation 5025, in which a first seed layer 1063 is formed over the lower conductive layer 1061. In some embodiments, the first seed layer 1063 may be formed in a single-layer form or a multi-layered form. In some embodiments, the first seed layer 1063 may be formed using CVD, PVD or ALD. In some embodiments, the first seed layer 1063 may be formed by ALD. In some embodiments, the first seed layer 1063 may be annealed prior to the formation of any further layer(s). In some embodiments, the first seed layer 1063 may be annealed by an in-situ annealing process. In some embodiments, after the annealing process, the first seed layer 1063 may have increased crystallinity.

Referring to FIG. 6D, in some embodiments, the operation 502 of the method 500 proceeds with operation 5027, in which a ferroelectric layer 1065 is formed over the first seed layer 1063. In some embodiments, the ferroelectric layer 1065 may be formed using sputtering, chemical solution deposition (CSD), pulsed laser deposition (PLD), CVD, PVD or ALD. In some embodiments, the ferroelectric layer 1065 is formed by ALD to achieve a thinner thickness, such as from approximately 0.1 nanometer to approximately 100 nanometers.

Referring to FIG. 6E, in some embodiments, after operation 5027, a second seed layer 1067 may be formed over the ferroelectric layer 1065. In some embodiments, the second seed layer 1067 may be formed in a single-layer form or a multi-layered form. In some embodiments, the second seed layer 1067 may be formed using CVD, PVD or ALD. In some embodiments, second seed layer 1067 is formed by ALD.

Referring to FIG. 6F, in some embodiments, the operation 502 of the method 100 proceeds with operation 5029, in which an upper conductive layer 1069 is formed over the ferroelectric layer 1065. In some embodiments, the upper conductive layer 1069 may be formed by using CVD, PVD or ALD, but the disclosure is not limited thereto. In some embodiments, the upper conductive layer 1069 may be annealed. In some embodiments, the upper conductive layer 1069 may be annealed by post metal annealing (PMA). In some embodiments, the upper conductive layer 1069 may be annealed by PMA at a temperature of from 400° C. to 900° C. In some embodiments, the upper conductive layer 1069 may be annealed by PMA in an ambient air of nitrogen, argon, oxygen or a combination thereof. In some embodiments, the upper conductive layer 1069 and the lower conductive layer 1061 may be annealed to have tensile stress, and thus may increase the crystallinity of the ferroelectric layer 1065. In some embodiments, the upper conductive layer 1069 and the lower conductive layer 1061 may include the same conductive material. In some alternative embodiments, the upper conductive layer 1069 and the lower conductive layer 1061 may include different conductive materials.

Referring to FIG. 6G, in some embodiments, the method 500 proceeds with operation 504, in which the layer stack is patterned to form a gate stack 106 over the substrate 102. In some embodiments, when the layer stack is patterned, the blocking layer 104 under the gate stack 106 may be patterned as well. In some embodiments, a photolithographic masking process may be performed to the layer stack to define a pattern of the gate stack 106 and the underlying blocking layer 104. In some embodiments, an etching process may be performed to the layer stack to removing a portion of the layer stack to form the gate stack 106 and the underlying blocking layer 104. In some embodiments, the etching process may include a wet etching process and a dry etching process, or a combination thereof. In some embodiments, the isolation structure 118 and portions of the substrate 102 may be exposed through the gate stack 106.

Referring to FIG, 6H, in some embodiments, the method 500 proceeds with operation 506, in which a spacer layer 108 is formed over side walls of the gate stack 106. In some embodiments, the spacer layer 108 may be formed over sidewalls of the blocking layer 104 as well. In some embodiments, the spacer layer 208 may be formed using CVD, PVD or ALD over top surface of the substrate 102, sidewalls of the gate stack 106 and the blocking layer 104, and top surface of the gate stack 106.

Referring to FIG. 6I, in some embodiments, an etching process may be performed on the spacer layer 108 to remove a portion of the spacer layer 108 so that a portion of the top surface of the substrate 102 and a portion of the top surface of the gate stack 106 may be exposed and sidewalls of the gate stack 106 and the blocking layer 104 may be covered by the spacer layer 108.

Referring to FIG. 6J, in some embodiments, the method 500 proceeds with operation 508, in which a patterned interlayer dielectric layer 114 may be formed over the substrate 102. In some embodiments, the interlayer dielectric layer 114 may be formed using CND, PND or ALD over the substrate 102 and the gate stack 106. In some embodiments, a photolithographic masking process may be performed to the interlayer dielectric layer 114 to define a source region contact pattern and a drain region contact pattern. In some embodiments, an etching process may be performed to the interlayer dielectric layer 114 to define a source region contact opening 120 o and a drain region contact opening 122 o, which expose portions of the top surface of the substrate 102, in some embodiments, the etching process may include a wet etching process and a dry etching process, or a combination thereof.

Referring to FIG. 6K, in some embodiments, the method 500 proceeds with operation 510, in which a source region 110 and a drain region 112 are formed within the substrate 102 through the patterned interlayer dielectric layer 114. In sonic embodiments, an implant process may be performed to the substrate 102 through the patterned interlayer dielectric layer 114 to form a source region 110 and a drain region 112 within the substrate 102. In some embodiments, during the implant process, plasma treatment of argon (Ar), hydrogen (H₂), nitrogen (N₂), helium (He) or a combination thereof may be performed to form high conductivity indium-rich (In-rich) regions in the source region 110 and the drain region 112, which may reduce contact resistance and may promote the formation of highly doped n¹⁺ regions.

Referring to FIG. 6L, in some embodiments, after the source region 110 and the drain region 112 are defined, a photolithographic masking process may be performed to the interlayer dielectric layer 114 to define a gate region contact opening 124 o. In some embodiments, an etching process may be performed to the interlayer dielectric layer 114 to define the gate region contact opening 124, which exposes a portion of the top surface of the gate stack 106. In some embodiments, the etching process may include a wet etching process and a dry etching process, or a combination thereof.

Referring to FIG, 6M, in some embodiments, a conductive material is filled within the source region contact opening 110 o, the drain region contact opening 112 o and the gate region contact opening 124 o using CVD, PVD or ALD. A planarization operation such as a. chemical-mechanical polishing (CMP) may be performed to remove superfluous materials. Accordingly, a source region contact 120, a drain region contact 122 and a gate region contact 124 are obtained, as shown in FIG. 6M.

In some embodiments, the lower conductive layer 1061 may be annealed prior to forming the first seed layer 1063. In some embodiments, the lower conductive layer 1061 may be annealed by a post metal annealing (PMA) process to enhance stress of the lower conductive layer 1061, in some embodiments, the PMA process may be performed at a temperature of from 400° C. to 900° C. In some embodiments, the PMA process may be performed in an ambient air of N₂, Ar, oxygen (O₂), or a combination thereof.

In some embodiments, the upper conductive layer 1069 may be annealed by a post metal annealing (PMA) process to enhance stress of the upper conductive layer 1069 and the crystallinity of the ferroelectric layer 1065. In some embodiments, the PMA process may be performed at a temperature of from 400° C. to 900° C. In some embodiments, the PMA process may be performed in an ambient air of N₂, Ar, oxygen (O₂). or a combination thereof.

In some embodiments, the first seed layer 1063 may be annealed prior to the formation of the ferroelectric layer 1065. In some embodiments, the first seed layer may be annealed by in-situ thermal annealing. In some embodiments, in-situ thermal annealing is performed at a temperature of from 400° C. to 700° C. In some embodiments, the in-situ annealing may be performed by substrate heating or an embedded IR heating kits around an apparatus, such as a chamber, in which the semiconductor structure 600 is located. In some embodiments, the in-situ annealing may be performed for a duration between approximately 1 minute and approximately 5 minutes. In some embodiments, crystallinity of the second seed layer 1065 may be improved by the in-situ annealing.

In some embodiments, the first seed layer 1063 may promote the remnant polarization (2 Pr, wherein 2 Pr=Pr⁺−Pr⁻) and crystallinity of the ferroelectric layer 1065. In some embodiments, the upper electrode 1069 and the low electrode 1061 may be formed with tensile stress to stabilize the ferroelectric layer 1065. In some embodiments, the upper electrode 1069 and the low electrode 1061 may be formed with tensile stress to stabilize the ferroelectric layer 1065 of o-phase, In some embodiments, the blocking layer 104 may reduce electron or hole injection from the channel, which is induced when a gate voltage larger than the threshold voltage is applied to the semiconductor structure 600, to the gate stack 106, and thus may reduce the leakage current flow from the channel formed within the substrate 102 to the gate stack 106 and may enhance the endurance and retention of the semiconductor structure 600.

In some embodiments, a second blocking layer (not shown) may be formed after the formation of the first seed layer 1063. In some embodiments, the second blocking layer may be formed prior to the formation of the second seed layer 1067. In some embodiments, the second blocking layer may be formed after the formation of the first seed layer 1063. In some embodiments, the second blocking layer may be formed between the formation of the first seed layer 1063 and the formation of the second seed layer,

Refer to FIGS. 7A to 7M. FIGS. 7A to 7M illustrate schematic cross-sectional views of a semiconductor structure 700 at various stages of fabrication in accordance with some embodiments of the present disclosure. The semiconductor structure 700 may include a substrate 302 as described above and as shown in FIG. 3. In some embodiments, a buffer layer 304 may be formed over the substrate 302 by PVD, CVD, or ALD. In some embodiments, a channel layer 306 may be formed over the buffer layer 304 by PVD, CVD, or ALD. In some embodiments, the operations carried out in the semiconductor structure 700 as shown in FIGS. 7A to 7M starting from the formation of the blocking layer 104 may correspond to those described above with respect to FIGS. 6A to 6M.

Refer to FIG. 8. FIG. 8 illustrates a schematic cross-sectional view of an integrated semiconductor structure 800 including a semiconductor structure 600 integrated with a field effect transistor (FET). In some embodiments, the forming of semiconductor structure 600 may be integrated with CMOS manufacturing operations. In such embodiments, a sum height H1 of a thickness of the gate stack 106 and a thickness of the blocking layer 104 may be similar to a height H2 of a gate structure 802 of an FET device, but the disclosure is not limited thereto. In some embodiments, the semiconductor structure 600 and the FET device may be electrically separated from each other by the isolation structure 118.

Accordingly, the present disclosure therefore provides a semiconductor structure and a method for forming the same. In some embodiments, the semiconductor structure may be an MFMIS memory structure. In some embodiments, the semiconductor structure includes a top-gate structure. In some embodiments, the semiconductor structure may be a self-aligned top-gate coplanar MFMIS memory structure. In some embodiments, the MFMIS memory structure includes a doped hafnium zirconium oxide blocking layer that may be formed by ALD. Accordingly, the doped hafnium zirconium oxide blocking layer may be doped with Si or other materials so as to form a high bandgap compared to the bandgap of the channel region to reduce electron or hole injection from the channel region to the gate stack of the MFMIS memory structure so as to reduce electro/hole current leakage, the negative-bias temperature instability (NBTI), the positive-bias temperature instability (PBTI) due to lower oxygen vacancies, and may enhance the endurance and retention of the MFMIS memory structure. In addition, the current leakage may be reduced with higher conduction band offset between channel and gate dielectric (V_(CBO)), and higher valence band offset between channel and gate dielectric (V_(VBO)).

Moreover, the MFMIS memory structure includes a seed layer between the lower electrode and the ferroelectric layer, which may promote the remnant polarization of the ferrolelectric layer. Furthermore, the crystallinity of the seed layer may be increased by annealing. Nonetheless, the electrodes with tensile stress may stabilizes the o-phase ferroelectric layer, such as the o-phase Hf_(x)Zr_(1-x)O₂ ferroelectric layer. None the less, the upper electrode and/or lower electrode are annealed, which may lead to the enhancement of the tensile stress of the upper electrode and/or lower electrode and the increase of the crystallinity of the ferroelectric layer disposed between the upper electrode and the lower electrode.

In some embodiments, a method for forming a semiconductor structure is provided. The method includes following operations. A channel layer is formed over a substrate. A layer stack is formed over the channel layer. The formation of the layer stack includes the following sub-operations: a blocking layer is formed over the channel layer, a lower conductive layer is formed over the blocking layer, a first seed layer is formed over the lower conductive layer, a ferroelectric layer is formed over the first seed layer, and an upper conductive layer is formed over the ferroelectric layer. The layer stack is patterned to form a gate stack over the channel layer. A pattered interlayer dielectric layer is formed over the channel layer and the gate stack. A source region and a drain region are formed in the channel layer through the patterned interlayer dielectric layer.

In some embodiments, a method for forming an integrated semiconductor structure is provided. The method includes following operations. At least two insolation structures are formed in a substrate. A layer stack is formed over the substrate. The formation of the layer stack includes the following sub-operations: a blocking layer is formed over the substrate, a lower conductive layer is formed over the blocking layer, a first seed layer is formed over the lower conductive layer, a ferroelectric layer is formed over the first seed layer, and an upper conductive layer is formed over the ferroelectric layer. The layer stack is patterned to form a plurality of gate stacks over the substrate, wherein the gate stacks are positioned between two adjacent isolation structures. A spacer layer is formed over sidewalls of the gate stacks, A pattered interlayer dielectric layer is formed over the substrate and the gate stacks. A source region and a drain region are formed for each of the gate stacks in the substrate through the patterned interlayer dielectric layer.

In some embodiments, a method for forming a semiconductor structure is provided. The method includes following operations. A layer stack is formed over the substrate. The formation of the layer stack includes the following sub-operations: a blocking layer is formed over the substrate, a lower conductive layer is formed over the blocking layer, a first seed layer is formed over the lower conductive layer, a ferroelectric layer is formed over the first seed layer, and an upper conductive layer is formed over the ferroelectric layer. The layer stack is patterned to form a gate stack over the substrate. A spacer layer is formed over sidewalls of the gate stack. A pattered interlayer dielectric layer is formed over the substrate and the gate stack. A source region and a drain region are formed in the substrate through the patterned interlayer dielectric layer.

The foregoing outlines features of several embodiments so that those skilled in the art may better understand the aspects of the present disclosure. Those skilled in the art should appreciate that they may readily use the present disclosure as a basis for designing or modifying other processes and structures for carrying out the same purposes and/or achieving the same advantages of the embodiments introduced herein. Those skilled in the art should also realize that such equivalent constructions do not depart from the spirit and scope of the present disclosure, and that they may make various changes, substitutions, and alterations herein without departing from the spirit and scope of the present disclosure. 

What is claimed is:
 1. A method for forming a semiconductor structure, comprising: forming a layer stack over a substrate, wherein the forming of the layer stack comprises: forming a blocking layer over the substrate, forming a lower conductive layer over the blocking layer; forming a first seed layer over the lower conductive layer; forming a ferroelectric layer over the first seed layer; and forming an upper conductive layer over the ferroelectric layer; patterning the layer stack to form a gate stack over the substrate; forming a spacer layer over side walls of the gate stack; forming a patterned interlayer dielectric layer over the substrate and the gate stack; and forming a source region and a drain region in the substrate through the patterned interlayer dielectric layer.
 2. The method of claim 1, further comprising annealing the lower conductive layer prior to forming the first seed layer.
 3. The method of claim 1, further comprising annealing the upper conductive layer.
 4. The method of claim 1, further comprising annealing the first seed layer prior to forming the ferroelectric layer.
 5. The method of Claim I further comprising forming a second seed layer over the ferroelectric layer prior to forming an upper conductive layer.
 6. The method of claim 1, further comprising forming a second blocking layer after forming the first seed layer.
 7. A method for forming a semiconductor structure, comprising: forming a channel layer over a substrate; forming a layer stack over the channel layer, wherein the forming of the layer stack comprises: forming a blocking layer over the channel layer, forming a lower conductive layer over the blocking layer; forming a first seed layer over the lower conductive layer; forming a ferroelectric layer over the first seed layer; and forming an upper conductive layer over the ferroelectric layer; patterning the layer stack to form a gate stack over the channel layer, forming a patterned interlayer dielectric layer over the channel layer and the gate stack; and forming a source region and a drain region in the channel layer through the patterned interlayer dielectric layer.
 8. The method of claim 7, further comprising annealing the lower conductive layer prior to forming the first seed layer.
 9. The method of claim
 7. further comprising annealing the upper conductive layer.
 10. The method of claim 7, further comprising annealing the first seed layer prior to forming the ferroelectric layer.
 11. The method of claim 7, further comprising forming a second seed layer over the ferroelectric layer prior to forming an upper conductive layer.
 12. The method of claim 7, further comprising forming a second blocking layer after forming the first seed layer.
 13. The method of claim 7, further comprising forming a buffer layer between the substrate and the channel layer.
 14. The method of claim 7, wherein the ferroelectric layer is formed by atomic layer deposition (ALD) to achieve a thickness of from approximately 0.1 nanometer to approximately 100 nanometers.
 15. A method for forming an integrated semiconductor structure, comprising: forming at least two insolation structures in a substrate; forming a layer stack over the substrate, wherein the forming of the layer stack comprises: forming a blocking layer over the substrate, forming a lower conductive layer over the blocking layer; forming a first seed layer over the lower conductive layer; forming a ferroelectric layer over the first seed layer; and forming an upper conductive layer over the ferroelectric layer; patterning the layer stack to form a plurality of gate stacks over the substrate, wherein the gate stacks are positioned between two adjacent isolation structures; forming a spacer layer over side walls of the gate stacks; forming a patterned interlayer dielectric layer over the substrate and the gate stacks; and forming a source region and a drain region for each of the gate stacks in the substrate through the patterned interlayer dielectric layer.
 16. The method of claim 15, further comprising annealing the lower conductive layer prior to forming the first seed layer.
 15. method of claim 15, further comprising annealing the upper conductive layer.
 18. The method of claim 15, further comprising annealing the first seed layer prior to forming the ferroelectric layer.
 19. The method of claim 15, further comprising forming a second seed layer over the ferroelectric layer prior to forming an upper conductive layer.
 20. The method of claim 15, further comprising forming a. second blocking layer after forming the first seed layer. 